ASTM B167 Inconel 600 / 601 Seamless Pipe Manufacturer
ASTM B167 Pipes / ASTM B167 Seamless Pipes / ASTM B167 Inconel 600 Seamless Pipes / ASTM B167 Inconel 601 Seamless Pipes / ASTM B167 UNS N06600 Seamless Pipes / ASTM B167 UNS N06601 Seamless Pipes / ASTM B167 Alloy 600 Seamless Pipes / ASTM B167 Alloy 601 Seamless Pipes
ASTM B167 - Seamless Pipe
ASTM B167 Seamless Pipes are often used in place of other stainless grades because they offer better corrosion resistance, better toughness, and better strength at high and low temperatures, and a range of special magnetic and electronic properties. The use of these grades practically eliminates crevice corrosion, and shows the best resistance to pitting corrosion. Nickel grades are also the best grades for high temperature applications, and as such are used for more demanding applications such as gas turbines and some chemical plants. Additionally, iron and nickel alloys are used in electronics and specialist engineering, while copper-nickel alloys are used for coinage and marine engineering.
Scope And Manufacturing
We at Mumbadevi Steel India (MSI) offer Nickel based seamless pipes adhering to ASTM B167 specifications possessing excellent properties like high strength, excellent heat resistance and resistance towards high temperature. These seamless pipes are highly applicable in aerospace industry and many commercial applications. Mumbadevi Steel India (MSI) also specializes in manufacturing and supplying SS904L and Duplex2205 in huge qualtity.
ASTM B167 Specification is standard specification which exclusively refers to Inconel 600 and Inconel 601 Seamless Pipe. The material should adhere to the ASTM B167 specified chemical composition limits for nickel, copper, iron, carbon, silicon, manganese and sulfur which should be further evaluated by chemical analysis.
ASTM B167 specification refers to Alloy 600 and Alloy 601 Seamless Pipes and Tubes. ASTM B167 UNS N06600 and ASTM B167 UNS N06601 are cold-worked annealed, hot-worked annealed, and hot-finished seamless pipes and tubes intended for general corrosion resistant and heat resistant applications.
Other Names : Inconel 600 Seamless Pipe, Inconel 600 Seamless Tubing, Inconel 601 Seamless Pipe, Inconel 601 Seamless tube, ASTM B167 UNS N06600, ASTM B167 UNS N06601.
Material : Inconel 600, Inconel 601
Brand : Mumbadevi Steel India (MSI)
Manufacturer : Mumbadevi Steel India (MSI)
Our Products: -
We at Mumbadevi Steel India (MSI) have huge inventory of Nickel based Seamless Tubing like ASTM B167 Inconel 600 Seamless Pipes and ASTM B167 Inconel 601 Seamless Pipes in various size, dimensions, and lengths. We also take pride in supplying customized order based on client's requirements.
|ASTM B167 Seamless Pipes|
|Seamless Pipe||Grade||UNS No||ASTM B167 Grade|
ASTM B167 Inconel 600/601 Seamless Pipe NB Sizes and Schedule Chart
|NB Sizes||Sch 5||Sch 10||Sch 40||Sch 80||Sch 160|
|ASTM B167 Inconel 600/601 Seamless Pipe 1/8″||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 1/4″||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 3/8″||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 1/2″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 3/4″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 1″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 1 1/4″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 1 1/2″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 2″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 2 1/2″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 3″||✔||✔||✔||✔||✔|
|ASTM B167 Inconel 600/601 Seamless Pipe 3″||✔||✔||✔||✔||✔|
Chemical Composition Limits:-
The material under this specification ASTM B167 should adhere to the specified chemical composition limits for specified elements like nickel, chromium, iron, manganese, aluminum, carbon, copper, silicon, sulfur, molybdenum, cobalt, boron, titanium, niobium, phosphorous, zirconium, yttrium, and cerium.
|Inconel 600||Inconel 601|
|Nickel||72.0 min||58.0 to 63.0|
|Chromium||14.0 to 17.0||21.0 to 25.0|
|Iron||6.0 to 10.0||Remainder|
|Manganese||1.0 max||1.5 max|
|Carbon||0.15 max||0.10 max|
|Copper||0.5 max||1.0 max|
|Silicon||0.5 max||0.5 max|
|Sulfur||0.015 max||0.015 max|
Mechanical Properties and Other Requirements:-
The ASTM B167 specifications requires material to adhere to following test methods performed on alloys, like chemical analysis, tension test, and hydrostatic or nondestructive electric test. The ASTM B167 specifications require material to conform to the following mechanical properties like Tensile strength, elongation, yield strength, and rounding methods.
|Grade Condition and Size||Tensile Strength, min, psi (MPa)||Elongation 2inches or 50.8mm or 4D min, %||Yield Strength (0.2% offset), min, psi (MPa)|
|Inconel 600 (UNS N06600):|
|5inches(127mm) in outside diameter and under||80 000 (550||35||30 000 (205)|
|Over 5inches(127mm) in outside diameter||75 000 (515)||35||25 000 (170)|
|5inches(127mm) in outside diameter and under||80 000 (550)||30||35 000 (240)|
|Over 5inches(127mm) in outside diameter||80 000 (550)||35||30 000 (205)|
|Inconel 601 (UNS N06601):|
|Cold-Worked Annealed or Hot-Worked Annealed :|
|All Sizes||80 000 (550)||35||30 000 (205)|
Flare Test: - The Flare test should consist of test specimen (one end of tube among the lot of 100) with the help of expanding tool having covering an angle of 60 degree, until the specified outside diameter of the tube is increased atleast by 30% from the original. During this process, the tube should not exhibit any cracking through walls.
Grain Size: - An n extended (transverse) sample exhibiting complete wall thickness of annealed alloys shall adhere to the average grain size as specified in ASTM B167 specification.
Hardness: - In stress-relived conditions when annealed ends are specified for tubing, the hardness of the ends should not cross the limits as specified in ASTM B167.
Hydrostatic or Nondestructive Electric Test: - Every tube should be put through either hydrostatic test or nondestructive electric test. Within the mentioned specification limits of outside diameter of 1/8 inches (3.2mm) and thickness of 0.015 inches (0.38mm), each tube should be tested to an internal hydrostatic pressure of 1000 psi. (6.9MPa). Fiber stress calculated using this formula should not exceed the specification limits.
Specimen Preparation: -
Tension test- The tubes in the final condition (temper) of production are taken as specimen for tension test, and are tested in the direction of fabrication. Tubes are tested in full tubular size or longitudinal strip with reduced gage lengths. The tension test should be performed on stress-relived tubes prior to annealing the ends.
Hardness test- The hardness test is performed on the inside of the tube near the end or on the specimen cut from the end.
Workman Ship, Finish and Appearance: -
ASTM B167 Seamless Tubings are individually covered so that the premium quality of material is retained and there are no damages in the last stages of production. The Tubings should be uniform in quality and temper, commercially straight, smooth and free of any imperfections.
Inspection: - The tubes should be inspected as agreed upon by the purchaser and the manufacturer.
Rejection and Rehearing: - The tube not adhering to the ASTM B167 specification or to authorized modifications should be subjected to rejection. The rejected specimens should be preserved for not less than 3 weeks from test report, and the manufacturer may claim for rehearing within that stipulated time period.
If it is mentioned in purchase order or the contract, then the manufacturer should be able to produce an certificate stating that the material has been manufactured and tested and inspected again with respect to the specification. It should also note the test results of the specimen samples which meets the specification requirements, and should be displayed as and when required.
ASTM B167 Seamless Tubes are tagged along with the imprints relevant to the job information which also contains information about the delivering destination like heat number, size, material, and part number.